Retention strength of cobalt-chromium vs nickel-chromium titanium vs CP titanium in a cast framework association of removable partial overdenture.

AIM: There is little information considering the framework association between cast clasps and attachments. The aim of this study was to evaluate the retention strength of frameworks match circumferential clasps and extra resilient attachment cast in three different alloys (cobalt-chromium, nickel-chromium titanium and commercially pure titanium), using two undercut (0.25 and 0.75 mm) and considering different period of time (0, 1/2, 1, 2, 3, 4 and 5 years). METHODS: Using two metallic matrices, representing a partially edentulous mandibular right hemiarch with the first molar crown, canine root and without premolars, 60 frameworks were fabricated. Three groups (n = 20) of each metal were cast and each group was divided into two subgroups (n = 10), corresponding the molar undercut of 0.25 mm and 0.75 mm. The nylon male was positioned at the matrix and attached to the acrylic resin of the prosthetic base. The samples were subjected to an insertion and removal test under artificial saliva environment. RESULTS: The data were analyzed and compared with ANOVAs and Tukey's test at 95% of probability. The groups cast in cobaltchromium and nickel-chromium-titanium had the highest mean retention strength (5.58 N and 6.36 N respectively) without significant difference between them, but statistically different from the group cast in commercially pure titanium, which had the lowest mean retention strength in all the periods (3.46 N). The association frameworks using nickel-chromium- titanium and cobalt-chromium could be used with 0.25 mm and 0.75 mm of undercut, but the titanium samples seems to decrease the retention strength, mainly in the 0.75 mm undercut. The circumferential clasps cast in commercially pure titanium used in 0.75 mm undercuts have a potential risk of fractures, especially after the 2nd year of use. CONCLUSION: This in vitro study showed that the framework association between cast clasp and an extra resilient attachment are suitable to the three metals evaluated, but strongly suggest extra care with commercially pure titanium in undercut of 0.75 mm. CLINICAL SIGNIFICANCE: Frameworks fabricated in Cp Ti tend to decrease in retentive strength over time and have a potential risk of fracture in less than 0.75 mm of undercut.

Influência da modificação do desenho de infraestruturas cerâmicas e metálicas na vida útil à fadiga e no modo de falha / Influence of modified framework design in all-ceramic and metal-ceramic crowns fatigue life and failure mode

Avaliar a influência da modificação do desenho da infraestrutura na vida útil à fadiga e no modo de falha em coroas metalo-cerâmicas e alumina infiltrada por vidro. Quarenta réplicas de um primeiro molar superior foram produzidas para receber coroas com infraestrutura padrão ou modificada. A infraestrutura modificada consistiu do desenho padrão (0,5 mm de espessura) aumentada por uma cinta lingual, unindo dois postes proximais. A carga (30-300 N) foi aplicada por um endentador metálico (3,18 mm raio) na superfície oclusal, durante 106 ciclos ou até a falha. A cada 125.000 ciclos o teste era interrompido para avaliar os danos. Fraturas catastróficas ou da porcelana de revestimento e a presença da trinca cone interno estendendo-se a infraestrutura foram os critérios utilizados para definir falha. As superfícies fraturadas e as polidas foram analisadas com estereomicroscópio e por microscopia eletrônica de varredura. A distribuição de Weibull foi utilizada para a análise estatística. A vida útil à fadiga da metalo-cerâmica foi significativamente maior que da alumina; contudo, a modificação não alterou este parâmetro nos grupos metálico ou cerâmico. Os grupos metalo-cerâmico apresentaram trincas cone interno sem fraturas da porcelana de revestimento. O grupo alumina com infraestrutura padrão apresentou principalmente fratura da porcelana de revestimento, enquanto que no grupo alumina com infraestrutura modificada se observou cone interno. A vida útil à fadiga não melhorou com a modificação no desenho das infraestruturas. O modo de falha variou de acordo com o material da infraestrutura.

To evaluate the effect of framework design on the fatigue life and failure modes of metal-ceramic and glass-infiltrated alumina. Forty composite resin tooth-replica of a prepared maxillary first molar were produced to receive crowns of a standard or modified framework design. Core design modification consisted of a standard, connecting to proximal struts. R-ratio fatigue loading was delivered with a spherical steel indenter (3.18 mm radius) on the center of the occlusal surface at a 30-300 N load range, until completion of 106 cycles or failure. Fatigue was interrupted every 125.000 cycles for damage evaluation. Catastrophic fracture, chipping within veneering porcelain, or inner cone crack reaching the core-veneer interface were the criteria for failure. Fractured and polished surfaces were characterized under light polarized microscopy followed by scanning electron microscopy. Weibull distribution fit was used for examining differences between groups. The highest fatigue life was observed for metal-ceramic crowns, but no significant differences were observed for groups with or without framework design modification. Failure modes of metal-ceramic comprised inner cone cracks without porcelain fracture. Glass-infiltrated alumina standard crowns presented bulk fracture whereas glass-infiltrated alumina modified crowns failed mainly through veneer. Fatigue life was not improved with framework design modification. Failure modes varied according to core material.

Effect of 2 percent iodine disinfecting solution on bond strength to dentin

INTRODUCTION: Disinfection of dentin surfaces is desirable so long as it does not interfere with subsequent bonding of adhesive resins. OBJECTIVE: To test the null hypothesis that bond strengths to dentin are not affected by previous application of an iodine disinfecting solution. MATERIALS AND METHODS: Twenty-four extracted non-carious molars were selected. Occlusal enamel was removed producing a flat dentin substrate. Test teeth were all treated with 2 percent Iodine disclosing/disinfecting solution (I2DDS) for 20 sec and rinsed for 20 sec followed by the application of self- or total- etching bonding systems, generating five adhesive groups (n=3): Single Bond; ; Prime & Bond NT; Clearfil SE Bond; Opti-Bond Plus. The control groups (n=3 per adhesive) had no disclosing/disinfectant application prior to adhesive application. A 4-mm thick resin restoration was built up on each tooth for microtensile testing. Statistical analyses between experimental and control groups were performed by student's t-test (alpha= 0.05). RESULTS: In general, experimental groups (previously treated with I2DDS) showed significantly lower bond strength values when compared with their respective controls (p<0.05), except for group Prime &Bond I2 that did not significantly differ from its control (p>0.05). CONCLUSION: Acetone-base adhesive systems seem not to be affected by the application of I2DDS prior to etching and bonding procedures.

INTRODUÇÃO: A desinfecção das superfícies de dentina é desejada desde que não haja interferência na adesão dos agentes adesivos. OBJETIVO: Testar a hipótese nula de que a resistência adesiva não é afetada pela aplicação prévia de uma solução desinfetante de iodo. MATERIAL AND MÉTODO: Vinte e quatro molares hígidos foram selecionados. O esmalte oclusal destes dentes foi removido, e sobre as superfícies planas de dentina expostas foi aplicada da solução desinfetante de Iodo a 2 por cento (I2DDS), que permaneceu sobre a superfície por 20 s e foi lavada por 20 s com água deionizada. Sobre as superfícies desinfetadas foram aplicados um dos seguintes sistemas adesivos (n=3): Single Bond; Prime & Bond NT; Clearfil SE Bond; Opti-Bond Plus. Os grupos controle (n=3) não tiveram a supeficie de dentina tratada com I2DDS antes dos precedimentos adesivos. Em todos os grupos, após hibridização da dentina, foi construída uma "restauração" de resina composta com cerca de 4 mm de espessura. Após 7 dias de armazenagem em água destilada, os dentes foram secionados de modo a originarem espécimes a serem submetidos ao teste de microtração (palitos). Análise estatística para comparação dos dados foi realizada pelo teste t de student (alfa=0,05). RESULTADOS: De forma geral, os grupos experimentais (tratados com I2DDS) apresentraram resistência adesiva significativamente menor do que os respectivos grupos controle (p<0.05), exceção se fez apenas para o grupo P&BI2, que não diferiu significativamente de seu grupo controle P&BC (p>0.05). Assim, a hipótese nula deve ser rejeitada para os adesivos a base de etanol e/ou a base de água, mas aceita para o adesivo a base de acetona. CONCLUSÃO: O uso da solução experimental de iodo previamente à realização dos procedimentos adesivos afetou a efetividade da união à dentina apenas quando do emprego de sistemas adesivos a base de etanol e/ou água.

Avaliação da resistência adesiva da interface de união em diferentes angulações empregando testes de microtração e análise dos elementos finitos / Evaluation of the microtensile bond strenght interface in different angles, testing the null hypothesis

Este estudo avaliou a resistência de união da interface adesiva, utilizando dois sistemas adesivos ("total-etching e self-etching"), testando diferentes ângulos da junção adesiva, com o teste de microtração e análise dos elementos finitos (AEF). Vinte e quatro molares hígidos recém extraídos foram selecionados e tiveram o esmalte oclusal removido perpendicularmente ao longo eixo dos dentes e foram divididos em dois grupos com 12 dentes, empregado-se no grupo 1 o adesivo Single Bond (3M-Espe Co.) e no grupo 2 o adesivo Clearfil SE Bond (Kuraray Co.). Restaurações de resina Z 100 com 4mm de espessura foram confeccionadas após a aplicação dos adesivos. Para realização dos testes de microtração foram obtidos espécimes com ângulos de 0o (controle), 10o, 20o e 30o na interface adesiva. O teste estatístico empregado foi ANOVA a dois critérios e teste de TUKEY. Foi realizada também análise dos elementos finitos, simulando as mesmas condições do teste de microtração. Os resultados mostraram uma diminuição dos valores da resistência adesiva à medida que a inclinação da interface adesiva aumentava sendo estatisticamente significante (p < 0.05) entre 0 e 30 graus de inclinação para o Clearfil SE Bond e entre 0 (controle) e 10, 20 e 30 graus de inclinação para o Single Bond, aceitado parcialmente a hipótese nula. Os resultados obtidos com AEF com a interface de 50 m e 100 m de espessura da camada adesiva mostraram uma tendência semelhante aos resultados obtidos com o teste de microtração